Nanoindentation of thin organic films and self-assembled monolayers

dc.contributor.advisorLiechti, K. M.en
dc.creatorWang, Mingjien
dc.date.accessioned2008-08-28T22:01:16Zen
dc.date.available2008-08-28T22:01:16Zen
dc.date.issued2004en
dc.descriptiontexten
dc.description.abstractIt has been established for some time now that interfaces between polymers and stiff substrates contain an interphase region (10 nm thick) where the properties of the polymer differ from those of the bulk. It has also been observed that interfacial cracks actually grow in these interphase regions. Thus it is important to understand the mechanical behavior of materials in such thin materials. Self-assembled monolayers (SAMs) provide well-controlled models for such studies. They are also important materials in MEMS devices where they are used for reducing friction and stiction. The SAM considered in this study was octadecyltrichlorosilane (OTS), which has a chain length of 2.6 nm. The OTS was probed with an interfacial force microscope (IFM). This relatively new device provides unambiguous force-displacement profiles in tension (adhesion) and compression (indentation). The IFM was also used to probe thicker films of (3-aminopropyl)triethoxysilane (γ-APS) so that a range of thickness could be considered. Thin γ-APS films and self-assembled OTS monolayers were deposited on Si(100) surfaces and characterized. A new approach for making OTS monolayers with nano-scale uniformity was developed. Some guidelines for the analysis of IFM experiments were drawn from a parametric study of layer and substrate interactions. Its high resolution in both force and displacement allows the IFM to be used to determine both the elastic mechanical and adhesive properties of thin films. Due to the different molecular structure of thin γ-APS films and selfassembled OTS monolayers, different analytical approaches were required. Combined experimental and continuum analyses of IFM nanoindentation of thin films, which accounted for the layer/substrate and adhesive interactions, were developed. A continuum analysis was used for γ-APS films, while a hybrid continuum-molecular analysis was required for OTS monolayers.
dc.description.departmentMechanical Engineeringen
dc.format.mediumelectronicen
dc.identifierb59363022en
dc.identifier.oclc58448640en
dc.identifier.proqst3151436en
dc.identifier.urihttp://hdl.handle.net/2152/1445en
dc.language.isoengen
dc.rightsCopyright is held by the author. Presentation of this material on the Libraries' web site by University Libraries, The University of Texas at Austin was made possible under a limited license grant from the author who has retained all copyrights in the works.en
dc.subject.lcshThin filmsen
dc.subject.lcshOrganic compoundsen
dc.subject.lcshNanotechnologyen
dc.titleNanoindentation of thin organic films and self-assembled monolayersen
dc.type.genreThesisen
thesis.degree.departmentMechanical Engineeringen
thesis.degree.disciplineMechanical Engineering.en
thesis.degree.grantorThe University of Texas at Austinen
thesis.degree.levelDoctoralen
thesis.degree.nameDoctor of Philosophyen

Access full-text files

Original bundle

Now showing 1 - 1 of 1
Loading...
Thumbnail Image
Name:
wangm81858.pdf
Size:
7.08 MB
Format:
Adobe Portable Document Format

License bundle

Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
1.65 KB
Format:
Plain Text
Description: