Underpotential deposition as a synthetic and characterization tool for core@shell dendrimer-encapsulated nanoparticles

The synthesis and characterization of Pt core/ Cu shell (Pt@Cu) dendrimer-encapsulated nanoparticles (DENs) having full and partial Cu shells deposited via electrochemical underpotential deposition (UPD) is described. Pt DENs containing averages of 55, 147, and 225 Pt atoms immobilized on glassy carbon electrodes served as the substrate for the UPD of a Cu monolayer. This results in formation of Pt@Cu DENs. Evidence for this conclusion is based on results from the analysis of cyclic voltammograms (CVs) for the UPD and stripping of Cu on Pt DENs, and from experiments showing that the Pt core DENs catalyze the hydrogen evolution reaction before Cu UPD, but that after Cu UPD this reaction is inhibited. Results obtained by in-situ electrochemical X-ray absorption spectroscopy (XAS) confirm the core@shell structure. Calculations from density functional theory (DFT) show that the first portion of the Cu shell deposits onto the (100) facets, while Cu deposits lastly onto the (111) facets. The DFT-calculated energies for Cu deposition on the individual facets are in good agreement with the peaks observed in the CVs of the Cu UPD on the Pt DENs. Finally, structural analysis of Pt DENs having just partial Cu shells by in-situ XAS is consistent with the DFT-calculated model, confirming that the Cu partial shell selectively decorates the (100) facets. These results are of considerable significance because site-selective Cu deposition has not previously been shown on nanoparticles as small as DENs. In summary, the application of UPD as a synthetic route and characterization tool for core@shell DENs having well defined structures is established. A study of the degradation mechanism and degradation products of Pd DENs is provided as well. These DENs consisted of an average of 147 atoms per dendrimer. Elemental analysis and UV-vis spectroscopy indicate that there is substantial oxidation of the Pd DENs in air-saturated solutions, less oxidation in N₂-saturated solution, and no detectable oxidation when the DENs are in contact with H₂. Additionally, the stability improves when the DEN solutions are purified by dialysis to remove Pd²⁺-complexing ligands such as chloride. For the air- and N₂-saturated solutions, most of the oxidized Pd recomplexes to the interiors of the dendrimers, and a lesser percentage escapes into the surrounding solution. The propensity of Pd DENs to oxidize so easily is a likely consequence of their small size and high surface energy. Calculations from density functional theory (DFT) show that the first portion of the Cu shell deposits onto the (100) facets, while Cu deposits lastly onto the (111) facets. The DFT-calculated energies for Cu deposition on the individual facets are in good agreement with the peaks observed in the CVs of the Cu UPD on the Pt DENs. Finally, structural analysis of Pt DENs having just partial Cu shells by in-situ XAS is consistent with the DFT-calculated model, confirming that the Cu partial shell selectively decorates the (100) facets. These results are of considerable significance because site-selective Cu deposition has not previously been shown on nanoparticles as small as DENs. In summary, the application of UPD as a synthetic route and characterization tool for core@shell DENs having well defined structures is established. A study of the degradation mechanism and degradation products of Pd DENs is provided as well. These DENs consisted of an average of 147 atoms per dendrimer. Elemental analysis and UV-vis spectroscopy indicate that there is substantial oxidation of the Pd DENs in air-saturated solutions, less oxidation in N2-saturated solution, and no detectable oxidation when the DENs are in contact with H2. Additionally, the stability improves when the DEN solutions are purified by dialysis to remove Pd2+-complexing ligands such as chloride. For the air- and N2-saturated solutions, most of the oxidized Pd recomplexes to the interiors of the dendrimers, and a lesser percentage escapes into the surrounding solution. The propensity of Pd DENs to oxidize so easily is a likely consequence of their small size and high surface energy.