SLS Fabrication of Highly Porous Model Including Fine Flow Channel Network Aiming at Regeneration of Highly Metabolic Organs

Fabrication of very porous scaffold for regeneration of highly metabolic organs is reported. Polycaprolactone (PCL) powder was mixed with fine salt grains as filler and SLS processed to develop a model including fine flow channel network. The fabricated model was rinsed with water to dissolve the salt, and high porosity of 90% was successfully obtained. Additionally, residual powder in the channels was effectively removed by solution of the filler. Through micro-CT observation, it was confirmed that channels of which diameter was smaller than 1mm were successfully fabricated and repeating branching and merging. Result of culture test is also reported.